Tensile strength

From Soft-Matter
Revision as of 15:30, 10 December 2011 by Redston (Talk | contribs)

Jump to: navigation, search

Entry by Emily Redston, AP 225, Fall 2011

Figure 1 Stress vs. Strain curve typical of aluminum 1. Ultimate strength 2. Yield strength 3. Proportional limit stress 4. Fracture 5. Offset strain (typically 0.2%) (http://en.wikipedia.org/wiki/Ultimate_tensile_strength)

The tensile strength (also called ultimate tensile strength) is the maximum stress that can be sustained by a structure in tension; if this stress is applied and maintained, the sample will fracture. It is important to note, however, that tensile strength is not necessarily the same as fracture strength. Let's consider the typical stress-strain curve of a ductile material, seen in Figure 1. You obtain such a curve by doing a tensile test, one of the most common mechanical tests. Tensile tests can be used to ascertain several important mechanical properties, such as the tensile strength of a material. For a ductile material, after yielding, the stress necessary to continue plastic deformation increases to a maximum, and then decreases to the eventual fracture point. The highest point of the stress-strain curve is the tensile strength, corresponding to point 1. All deformation up to this point is uniform through the narrow region of the tensile specimen. However, at this maximum stress, a small constriction or neck begins to form (typically near the middle of the sample), and all subsequent deformation is confined at this neck. This phenomenon is termed "necking", and fracture ultimate occurs at the neck. Fracture strength corresponds to the stress at fracture. It is clear that the tensile strength is not the same as the fracture strength in this case. However, for brittle materials, these will tend to be more similar. In brittle materials, the UTS will at the end of the linear-elastic portion of the stress-strain curve or close to the elastic limit. In ductile materials, the UTS will be well outside of the elastic portion into the plastic portion of the stress-strain curve.

Tensile strength is defined as a stress, which is measured as force per unit area. It is typically reported in units Pa or psi. The tensile strength is an intensive property, meaning that its value does not depend on the size of the test specimen. However, it is dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.

The UTS may not be completely representative of the highest level of stress that a material can support, but the value is not typically used in the design of components anyway. For ductile metals the current design practice is to use the yield strength for sizing static components. However, since the UTS is easy to determine and quite reproducible, it is useful for the purposes of specifying a material and for quality control purposes. On the other hand, for brittle materials the design of a component may be based on the tensile strength of the material.

Typical tensile strengths

Typical tensile strengths of some materials (from [2])
Material Yield strength
Ultimate strength
Structural steel ASTM A36 steel 250 400 7.8
Carbon steel 1090 250 841 7.58
Human skin 15
Steel, high strength alloy ASTM A514 690 760 7.8
High density polyethylene (HDPE) 26-33 37 0.95
Polypropylene 12-43 19.7-80 0.91
Stainless steel AISI 302 - Cold-rolled 520 860 8.19
Cast iron 4.5% C, ASTM A-48 130 200  
Aluminium alloy 6063-T6   248 2.63
Copper 99.9% Cu 70 220 8.92
Cupronickel 10% Ni, 1.6% Fe, 1% Mn, balance Cu 130 350 8.94
Brass 200 + 550 5.3
Tungsten   1510 19.25
E-Glass N/A 1500 for laminates,
3450 for fibers alone
S-Glass N/A 4710 2.48
Marble N/A 15  
Concrete N/A 3 2.7
Carbon fiber N/A 1600 for Laminate,
4137 for fiber alone
Human hair   380  
Bamboo   350-500 0.4
Spider silk 1000 1.3
Silkworm silk 500   1.3
Aramid (Kevlar]] or Twaron) 3620 2757 1.44
23 46 0.97
Vectran   2850-3340  
Pine wood (parallel to grain)   40  
Bone (limb) 104-121 130 1.6
Nylon, type 6/6 45 75 1.15
Rubber - 15  
Boron N/A 3100 2.46
Silicon, monocrystalline (m-Si) N/A 7000 2.33
Silicon carbide (SiC) N/A 3440  
Sapphire (Al2O3) N/A 1900 3.9-4.1
Boron Nitride Nanotube N/A 33000  ?
Diamond N/A 2800 3.5
First carbon nanotube ropes  ? 3600 1.3
Colossal carbon tube N/A 7000 0.116
Carbon nanotube N/A 11000-63000 0.037-1.34


[1] Callister, William D. Materials Science and Engineering: an Introduction. New York: John Wiley & Sons, 2007.

[2] http://en.wikipedia.org/wiki/Ultimate_tensile_strength