Reversible Switching of Hydrogel-Actuated Nanostructures into Complex Micropatterns

From Soft-Matter
Revision as of 02:48, 25 February 2009 by Ichthus (Talk | contribs) (Soft matter example)

Jump to: navigation, search

By Sung Hoon Kang

Title: Reversible Switching of Hydrogel-Actuated Nanostructures into Complex Micropatterns

Reference: Alexander Sidorenko,Tom Krupenkin, Ashley Taylor, Peter Fratzl, Joanna Aizenberg, Science 315, 487-490 (2007).

Soft matter keywords

hydrogel, humidity, artificial muscle

Abstract from the original paper

Responsive behavior, which is intrinsic to natural systems, is becoming a key requirement for advanced artificial materials and devices, presenting a substantial scientific and engineering challenge. We designed dynamic actuation systems by integrating high–aspect-ratio silicon nanocolumns, either free-standing or substrate-attached, with a hydrogel layer. The nanocolumns were put in motion by the “muscle” of the hydrogel, which swells or contracts depending on the humidity level. This actuation resulted in a fast reversible reorientation of the nanocolumns from tilted to perpendicular to the surface. By further controlling the stress field in the hydrogel, the formation of a variety of elaborate reversibly actuated micropatterns was demonstrated. The mechanics of the actuation process have been assessed. Dynamic control over the movement and orientation of surface nanofeatures at the micron and submicron scales may have exciting applications in actuators, microfluidics, or responsive materials.

Soft matter example

In this paper, the authors used combination of soft and hard elements for reversible actuation of rigid nano- and microstructures whose motion was controlled by the polymer layer. They combined a hydrogel with an array of isolatedd high aspect ratio rigid structures (AIRS) into hydrogel-AIRS assemblies (HAIRS) as shown in Fig 1. In this system, the ARIS gives structural rigidity whereas the soft hydrogel gives reponsive behavior to external stimuli.

The details of the fabrication procedure are described in the text and the supplemental information. The geometry of the AIRS used in this paper is consisted of square arrays of nanoposts with diameters d = 100 to 300 nm, heights h = 5 to 8 um, aspect ratios h/d = 15 to 80, and periodicities p = 2 to 4 mm.

Fig. 1 (A) Schematic presentation of the structure and composition of the PAAG film grafted to the Si/SiO2<\sub> substrate via the PGMA anchoring layer. (B) Scanning electron micrograph (SEM) of a sample AIRS structure composed of an array of silicon nanocolumns. An inset on the right reveals a banding pattern (scalloping) that is characteristic of the Bosch fabrication process. The band width is ~200 nm. (C) Hydrogel synthesis in the confinement of the AIRS and a secondary substrate (a glass slide or a silicon wafer, either flat or topographically patterned) separated by a spacer of the desired thickness that regulates the size of the polymer film. (D) Hybrid HAIRS-1 design. The nanocolumns, embedded into the hydrogel layer grafted to the PGMA-modified confining surface, break from the original wafer upon the separation of the confining substrates and become fully transferred onto the secondary surface. The surface topography changes from an array of highly tilted to vertically oriented nanocolumns. (E) Hybrid HAIRS-2 design. The hydrogel film is attached directly to the AIRS silicon wafer. Nanocolumns remain attached to the surface and bend upon drying.