Fabrication of Hierarchical Structures by Wetting Porous Templates with Polymer Microspheres

From Soft-Matter
Revision as of 18:18, 18 September 2009 by Bonificio (Talk | contribs) (Soft matter discussion)

Jump to: navigation, search

Original entry: William Bonificio, AP 225, Fall 2009

Information

Fabrication of Hierarchical Structures by Wetting Porous Templates with Polymer Microspheres Jiun-Tai Chen, Dian Chen, Thomas P. Russell Langmuir 2009 25 (8), 4331-4335


Soft matter keywords

Polystyrene, microspheres, heirarchical structure, glass transition temperature

Summary

The researchers used a very simple method using capillarity to create a hierarchical structure. Polystyrene spheres were first allowed to self assemble over a silicon substrate, this being the first length scale of the structure. After this a nanoporous sheet of aluminum was placed over the top of the spheres. The spheres were then heated above their glass transition temperature. At this point capillary action occurred within the pores on the polystyrene, causing the polystyrene to rise up into the spheres. This created many 'bumps' on the spheres - giving rise to the second length scale of the hierarchical structure.

Soft matter discussion

Two soft matter phenomenons of self assembly and capillarity were utilized by the researchers in this experiment to create their hierarchical structure.

First, a suspension of polystyrene spheres in ethanol was placed on a clean silicon wafer, and allowed to dry over night. As the ethanol evaporated the spheres self assembled into an hexagonal monolayer across the wafer. This occurred because of the capillary forces driving the polystyrene together as the ethanol evaporated. Different experiments were performed using different radii from .3 to 2 microns.

After this, an aluminum template that had 50nm pores spaced 100nm apart was placed over the top. The system was then heated to a temperature above the polystyrene glass transition temperature (Tg for polystyrene = 378K) and the researchers allowed capillary forces to do their work, lifting the polystyrene into the pores of the aluminum to form nanopores. The flow rate of the polymer melt in the pores can be calculated using the following equation:

<math>\frac{dz}{dt} = \frac{R\gamma cos \theta }{4 \eta z}</math>

where z is the height, t is the time, R is the radius of the nanopores, <math>\gamma</math> is the surface tension, and <math>\eta</math>η is the viscosity

 The aluminum template was subsequently dissolved, leaving the polystyrene spheres behind.