Controlled Switching of the Wetting Behavior of Biomimetic Surfaces with Hydrogel-Supported Nanostructures

From Soft-Matter
Revision as of 22:09, 8 February 2009 by Stsai (Talk | contribs)

Jump to: navigation, search

By Lidiya Mishchenko


In this paper, Aizenberg et. al. utilized nanopost arrays to allow structures to switch between wetting and non-wetting states (superhydrophobic and not). These arrays (as synthesized) are silicon nanostructures with high aspect ratio features. When coated with a hydrophobic silane, they demonstrate superhydrophobicity (through coupling of high contact angle and structure). The behavior of a device that switches from nonwetting to wetting in a humid environment was called "direct response" and one that switches from wetting to non-wetting in a humid environment was called "reverse response" (See captions).

Direct Response: Nanposts attached to substrate. During dry state, we have cassie a state (superhydrophobic) because the posts are covered with a hydrophobic silane and the hydrogel is not in contact with the droplet. During the wet state, the hydrogel swells and the water droplet comes into contact with the hydrophillic hydrogel, allowing wetting.
Reverse Response: Nanoposts embedded in hydrogel but not attached to substrate. During drying, hydrogel contracts and tilts posts, allowing for wetting (breaking the Cassie state). When hydrogel is wet, the nanoposts point straight up (restoring the Cassie state hydrophobicity).


A large portion of the paper focused on creating a hydrogel layer that was anchored properly to the substrate and could reversibly switch for many cycles.

Some interesting ideas in the paper:

- Hydrogels were defined as "responsive materials composed of cross-linked flexible polymeric hydrophillic chains whore elastic networks can swell in water to the desired degree of hydration"

-They noted that hydrogels are "shape-memory" polymers and this allows for the repeatability of the process. Also noted was that hydrogels respond to a variety of stimuli: humidity, pH, etc.

-In their intro, they gave a nice definition of superhydrophobicity: "a very high water droplet contact angle and a very small advancing-receding hysteresis... a water droplet deposited on a superhydrophobic surface maintains its almost spherical shape and easily slides over the surface"

-The bio-inspiration for responsive superhydrophobic structures comes from: legs of water spiders and beetles. They use nanostructured hydrophobicity for "water repellence, movement, and water capture"

-Finally, they mentioned another paper that demonstrates (for block copolymer coatings) "water-induced increase of superhydrophobicity of the polymer coatings...caused by the dynamic rearrangement of the flourinated polymer segments" [[1]] Makal, U. and, Kenneth J. Wynne. Water Induced Hydrophobic Surface. Langmuir 2005 21 (9), 3742-3745



By Scott Tsai


Overview

In this paper, Sidorenko et al demonstrated a hybrid system of rigid nanostructures with responsive hydrogel films to create a superhydrophobic-hydrophilic switch. They demonstrate this for two cases. The first case is for a "direct response", where the unactuated state of the system is superhydrophobic, and the second case is for a "reverse response", where the unactuated state of the system is hydrophilic.


Si Nanostructured Surfaces

Fig.1 A SEM photograph of the Si structures and B what a droplet of water looks like as it sits on the nanostructured surface
Krupenkin et al had recently fabricated Si nanostructures that were coated with a hydrophobic coating. The result was what the authors termed "superhydrophobicity", where water that was placed on the surface displayed very high contact angles and very small contact line hysteresis.<ref>
















References

1. T. Krupenkin, J. A. Taylor, T. M. Schneider and S. Yang, Langmuir, 2004, 20, 3824-3827